Large Diameter Borosilicate Glass Tubing Temperature Resistant SGS

Good Chemical Temperature Borosilicate Glass Tubing

raw material

Including main raw materials and auxiliary raw materials. The former refers to the introduction of raw materials such as the oxides that form the network structure of the glass, the intermediate oxides and the oxides outside the network; the latter can accelerate the melting of the glass or make it obtain certain necessary properties.

main ingreadient

According to the nature of the introduced oxides, it is divided into acidic oxide raw materials, alkali metal oxide raw materials and alkaline earth metal oxide raw materials.
① Acidic oxide raw materials: raw materials such as SiO2, B2O3, Al2O3, etc. SiO2 is the skeleton of the glass structure in silicate glass. It gives the glass high strength, good chemical stability, heat resistance and low expansion, but it will increase the melting temperature of the glass and increase the viscosity. The cited raw materials of SiO2 are silica sand, sandstone, and quartzite. Adding B2O3 to the glass can reduce the thermal expansion of the glass, increase the refractive index, thermal shock resistance and chemical resistance, reduce the viscosity of the glass when the temperature is higher, and increase the viscosity of the glass when the temperature is lower. The cited raw material for B2O3 is borax or boric acid. Adding Al2O3 to the glass can reduce the tendency of glass to crystallize and enhance the chemical stability, increase the strength, and increase the viscosity of the glass. The cited raw materials are usually feldspar with K2O or Na2O and SiO2, and industrial alumina can also be used. Cangzhou Tianchang Craft Glass Products Factory specializes in the production of various types of high borosilicate glass tubes
② Alkali metal oxide raw materials: raw materials with Na2O and K2O. Adding Na2O and K2O to the glass can reduce the melting temperature and viscosity, but it will make the chemical stability of the glass worse. The cited raw materials are soda ash (Na2CO3) and potash (K2CO3).

It mainly includes the steps of batch preparation, melting, forming, annealing and post-processing.

Batch preparation

First, the raw material pretreatment includes pulverization of bulk material, pre-wetted material is dried, treated iron-containing materials in addition to iron, and the like. The particle size after pulverization should be 0.25 ~ 0.5mm. Too coarse particles are not easily melted sufficiently, the remaining powder will form stone or silicon rich nodules in the glass; too fine particles are easily scattered or agglomerated into clumps. The particle size of the raw materials according to a certain formula is precisely weighed, and then mixed with a tumbler, mixer paddle or disc.
MeltingGlass batch melting and refining at an elevated temperature to form a homogeneous molten glass free of bubbles, no stones. The melting Temperature of the glass frit varies with the composition, typically 1300 ~ 1600 ℃. Batches go through a series of physical and chemical reactions and gradually melt completely at high temperatures. With increasing temperature, the viscosity decreased significantly large amount of gas and feed air contained therein escapes decomposition increase the melt, a clear melt. Removing bubbles temperature, chemical composition of the molten glass tends to be uniform. If necessary, apply mechanical external force to stir. After completion of cooling a clear homogeneous, uniformly achieve a desired glass viscosity suitable for forming.
In the glass melting furnace. Continuous melting in the kiln during mass production. One end of a batch kiln was added, the molten glass forming the other end of the discharge. In small batches, batches melted in a crucible furnace.

Our Company:

Since its establishment, the four-star company has always adhered to the purpose of "dedicating itself to the development of pharmaceutical industry and ensuring the safety of people's medication", the business philosophy of "taking integrity as the foundation, survival by quality and development by innovation", and the quality policy of "scientific management, careful manufacturing, high-quality service and excellence". All employees work hard with one heart and one mind, In the fierce market competition, we overcome difficulties, forge ahead bravely, and continue to develop and grow.